The influence of porosity on the transverse rupture strength (TRS) in sintered compacts of aluminum powder was studied. Green compacts (non sintered) made previously with metallic powder of the Al-1,25%Mn-1,1%Fe alloy were used. The powder particles were classified in function of size and 50% were mixed with lubricant. The solid-state sintering was carried out.  That the porosity is characterized by a structure of interlocked open pores was determined. The bigger porosity was found in the sintered compacts that initially had lubricated particles. That the transverse rupture strength is proportional inversely to the porosity was established, independently of the particles and pores characteristics. The deformation capacity (flexion) is smaller and practically of constant value in the sintered compacts with bigger porosity.Se estudió la influencia que tiene la porosidad sobre la resistencia a la rotura transversal (RRT), en compactos sinterizados de polvo de aluminio. Se utilizaron compactos verdes (no sinterizados) fabricados previamente con polvo metálico de la aleación Al-1,25%Mn-1,1%Fe, cuyas partículas fueron clasificadas en función del tamaño y el 50%  se mezclaron con lubricante. Se realizó la sinterización en estado sólido. Se determinó que la porosidad se caracteriza por una estructura de poros abiertos interconectados. La mayor porosidad se encontró en los compactos sinterizados que inicialmente tenían partículas lubricadas. Se estableció que la resistencia transversal a flexión es inversamente proporcional a la porosidad, independientemente de las características de las partículas y de los poros. La capacidad de deformación (flexión) es menor y prácticamente de valor constante en los compactos sinterizados con mayor porosidad.