In this work, the mechanical behavior of stainless steel rebars was experimentally evaluated, as a function of their degree of corrosion, in comparison with the mechanical behavior of carbon steel. For this purpose, 16 mm diameter rebars of stainless steel and carbon steel, corroded in an accelerated way in a previous stage and with the presence of chloride ion as a triggering factor, were subjected to tensile tests in order to study the effect of corrosion on their mechanical properties and ductility based on the concept of equivalent steel. From the results it was possible to verify that the influence of corrosion on stainless steels is much lower than that of carbon steel, complying with the minimum values established in the European standards for reinforced concrete structures (CM-90, EC2 and EHE).En este trabajo se evaluó experimentalmente el comportamiento mecánico de armaduras de acero inoxidable y al carbono en función de su grado de corrosión, en comparación con el comportamiento mecánico del acero al carbono. Para ello se sometieron a ensayos de tracción barras corrugadas de acero inoxidable y acero al carbono de 16 mm de diámetro corroídas de forma acelerada en una etapa anterior y con un factor desencadenante la presencia del ion cloruro, con el fin de estudiar el efecto de la corrosión sobre sus propiedades mecánicas y su ductilidad en base al concepto de acero equivalente. A partir de los resultados se pudo comprobar que la influencia de la corrosión a los aceros inoxidables es mucho menor a los del acero al carbono, cumpliendo con los valores mínimos que se establecen en la normativa europea con respecto a estructuras de hormigón armado (CM-90, EC2 y EHE).