Efecto de fibras de acero en resistencia a compresión, flexión y módulo de elasticidad en hormigones simples de 21 MPa
Fecha
2022-08Autor
Sarango Pinzón, Marlon José
Toapanta Andachi, Wellington Wladimir
Institución
Resumen
This current academic article has aim to analize the
effects of additioning steel fibers Dramix 3D to
simple concrete that was dosified for a resistence of
21MPa. The steel fibers are a bit unknown and not
so common in the construction trade that is why its
acquisition is not easy. This research is focused on
three parameters that are part of mechanical
platform traits which are: compression resistence,
flexion resistence and elasticity module. The
methodology used for this work is neatly
experimental, parting from a dosificaction base; it
was added different steel-fiber dosification on base
to the total platform volumen. The obtained results
with the steel fibers were analized and compared
with the base concrete obtained results. Parting
from the obtained results it was elaborated a
correlatión between resistence and compression and
the breaking module which is exposed on a
polinomic formula. Through experimentation it was
concluded that the steel fibers help to improve the
concrete mechanical propertien , which is why the
use of these steel fibers is recommended. All the
results will be exposed all through this document.