Photosensitization of thin SnO2 nanocrystalline semiconductor film electrodes with electron donor-acceptor metallodiporphyrin dyad
Fecha
2005-06Registro en:
Gervaldo, Miguel Andres; Otero, Luis Alberto; Milanesio, María Elisa; Durantini, Edgardo Néstor; Silber, Juana J.; et al.; Photosensitization of thin SnO2 nanocrystalline semiconductor film electrodes with electron donor-acceptor metallodiporphyrin dyad; Elsevier Science; Chemical Physics; 312; 1-3; 6-2005; 97-109
0301-0104
CONICET Digital
CONICET
Autor
Gervaldo, Miguel Andres
Otero, Luis Alberto
Milanesio, María Elisa
Durantini, Edgardo Néstor
Silber, Juana J.
Sereno, Leonides Edmundo
Resumen
A electron donor-acceptor porphyrin dyad (PZn-P) was synthesized by linking an electron acceptor porphyrin; 5,15-bis(4-carboxyphenyl)-10,20- bis(4-nitrophenyl) porphyrin (P) and an electron donor porphyrin; Zn(II) 5-(4-aminophenyl)-10,15,20-tris(4-methoxylphenyl) porphyrin (PZn) by amide bond. PZn-P dyad - thin SnO2 nanocrystalline semiconductor film electrodes show higher spectral sensitized photocurrent quantum yield compared to the electrodes sensitized with either PZn or P monomers. Fluorescence analysis of dyad and the P moiety adsorbed on both, SnO2 semiconductor and SiO2 insulator, shows that the charge injection yields (Φinj) from the excited dyes to the SnO2 are similar in both cases. Thus photocurrent enhancement is interpreted in terms of intramolecular electron transfer and preferential spatial orientation of the dyad on the SnO2 surface that preclude back electron transfer.