Nanoestructuras de sílice, con diámetro y distribución de mesoporos variable, modificadas con ácido tungstofosfórico como catalizadores en la síntesis de quinoxalinas
Silica nanostructures, with variable diameter and mesopore size distribution, modified with tungstophosphoric acid as catalyst in the synthesis of quinoxalines;
Nanoestruturas de sílica, com distribuição variável de diâmetro e tamanho de
mesoporos, modificadas com ácido tungstofosfórico como catalisador na síntese de a síntese da quinoxalina
Fecha
2020-05Registro en:
Sosa, Alexis Alberto; Romanelli, Gustavo Pablo; Pizzio, Luis Rene; Nanoestructuras de sílice, con diámetro y distribución de mesoporos variable,
modificadas con ácido tungstofosfórico como catalizadores en la síntesis de quinoxalinas; Universidad Nacional de Colombia; Revista Colombiana de Química; 49; 2; 5-2020; 37-43
0120-2804
2357-3791
CONICET Digital
CONICET
Autor
Sosa, Alexis Alberto
Romanelli, Gustavo Pablo
Pizzio, Luis Rene
Resumen
Se sintetizaron catalizadores (SNX#WPA) basados en ácido tungstofosfórico, en soportes de nanoestructuras de sílice (SNX), con distribución de diámetros y tamaños de mesoporos variables. Las SNX se prepararon en medio de octano/agua, usando poliestireno y bromuro de cetiltrimetilamonio como plantillas. Los materiales se caracterizaron por DRX, TEM y adsorción/desorción de nitrógeno. La relación octano/agua influyó tanto en la morfología y el tamaño de las SNX como en la distribución del tamaño de poro. Las SNX obtenidas utilizando relaciones OCT/H2 O en el rango de 0,07-0,35, presentan mesoporos pequeños (5-6 nm) y grandes (28-34 nm), generados principalmente por poliestireno. Los mesoporos grandes y su contribución de volumen fueron claramente más altos que en las muestras SN1, SN2 y SN3. La estructura y la morfología de SNX#WPA fueron similares a las de las SNX usadas como soporte. Además, la caracterización de todos los materiales SNX#WPA por FT-IR y 31P NMR indicó la presencia de especies [PW12O40]3− y [H3- XPW12O40](3-X)− sin degradar. Según los resultados de la valoración potenciométrica, los sólidos presentaron sitios ácidos muy fuertes. Se evaluó la actividad de SNX#WPA como catalizadores en la síntesis de quinoxalinas, a partir de lo cual se obtuvieron altos rendimientos, sin formación de subproductos. De ello resultó que los materiales preparados son catalizadores altamente selectivos y reutilizables. Tungstophosphoric acid supported on silica nanostructures (SNX#WPA) with variable diameter and mesopore size distribution were synthetized. Silica nanostructures (SNX) were prepared in octane/aqueous media using polystyrene and CTAB as organic templates. The materials were characterized by XRD, SEM, TEM and dinitrogen adsorption/ desorption isotherm analysis. The octane/ water ratio influenced the morphology and size of SNX prepared, as well as its pore size distribution. The SNX samples obtained using OCT/H2 O ratios in the range 0.07-0.35 (SN4, SN5, and SN6 samples). present small (5-6 nm) and large (28-34 nm) mesopores (mainly generated by polystyrene). Large mesopores and their volume contribution were clearly higher than in the SN1, SN2, and SN3 samples. The structure and morphology of SNX#WPA samples were similar to those of the SNX. Furthermore, the characterization of all the SNX#WPA materials by FT-IR and 31P NMR indicated the presence of undegraded [PW12O40]3− and [H3-XPW12O40](3-X)− species. According to the potentiometric titration results, the solids presented very strong acid sites. The performance of SNX#WPA materials as catalysts in the synthesis of quinoxalines was evaluated. The yields achieved were high, without formation of by-products resulting from competitive reactions or decomposition products, so the prepared materials are highly selective and reusable catalysts. Catalisadores (SNX#WPA) baseados em ácido tungsofosfórico suportado em nanoestruturas de sílica (SNX) foram sintetizados com distribuição de tamanhos e diâmetros variados de mesoporos. Os SNX foram preparados em meio octano/aquoso usando poliestireno e brometo de cetiltrimetilamônio como modelos orgânicos. Os materiais foram caracterizados por DRX, TEM e adsorção/ dessorção de nitrogênio. A razão octano/ agua influenciou a morfologia e o tamanho do SNX, bem como a distribuição do tamanho dos poros. O SNX obtido usando razões OCT/ H2 O na faixa de 0,07-0,35, possui mesoporos pequenos (5-6 nm) e grandes (28-34 nm) (gerados principalmente por poliestireno). Mesoporos grandes e sua contribuição em volume foram claramente maiores do que nas amostras SN1, SN2 e SN3. A estrutura e a morfologia do SNX#WPA foram semelhantes às do SNX usado como suporte. Além disso, a caracterização de todos os materiais SNX#WPA por FT-IR e 31P NMR indicou a presença das espécies [PW12O40]3− e [H3- XPW12O40](3-X)− sem degradar. De acordo com os resultados da titulação potenciométrica, os sólidos apresentaram locais ácidos muito fortes. A atividade do SNX#WPA como catalisadores na síntese de quinoxalinas foi avaliada, produzindo altos rendimentos, sem formação de subprodutos, resultando em materiais catalisadores altamente seletivos e reutilizáveis