Estabilización de espumas de aluminio con partículas de alúmina metalizadas con cobre
Fecha
2012-02Autor
Monje García, Miguel Ángel
Resumen
In general, a process of foam from foamable compacted consists of three basic steps: formation of pores; growth; and collapsing. In this work, the addition of alumina particles to the porous structure being investigated to slow collapsing phenomenon which manifests itself in a foamed liquid due to the coalescence of aluminum pores and drained by gravity. Alumina influences the interfacial forces, the viscosity and the wall thickness between the pores; the drawback in the Al-Al2O3 system is the wettability of the ceramic void by the liquid metal, which causes the aluminum to alumina eject the cellular structure. De manera general, un proceso de espumado a partir de compactados espumables consiste en tres etapas básicas: formación de poros; crecimiento; y colapsamiento. En el presente trabajo se investiga la adición de partículas de alúmina a la estructura porosa para retardar el colapsamiento, fenómeno que se manifiesta en un líquido espumado debido a la coalescencia de poros y drenado del aluminio por acción de la gravedad. La alúmina influye en las fuerzas interfaciales, en la viscosidad y en el espesor de las paredes entre los poros; el inconveniente en el sistema Al-Al2O3 radica en la nula mojabilidad del cerámico por el líquido metálico, lo que provoca que el aluminio eyecte a la alúmina de su estructura celular.