articuloAlumina-lanthana (La at 1, 3, or 5 wt%) supports were prepared by sol-gel from Al alkoxide sol where La(NO 3 ) 3 was added. Annealed (550 °C) xerogels were characterized by N 2 physisorption, thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy- energy dispersive spectroscopy (SEM-EDS), CO 2 -adsorption studied in IR region, Raman and ultraviolet-vis (UV-vis) spectroscopies. The texture of amorphous binary matrices of high La dispersion was adequate to applications in catalysts for middle distillates hydrodesulfurization (HDS). Generally, the amount and strength of surface basic sites increased with La content in solids. Mo (at 2.8 at. nm −2 ) and Co (at Co/(Co+Mo) = 0.3) were deposited over carriers by one-pot simultaneous impregnation in the presence of PO 4 3− (P 2 O 5 /(NiO+MoO 3 ) = 0.2 mass ratio). Calcined (400 °C) Co-Mo-P impregnated precursors had decreased basicity as to that of corresponding carriers, suggesting strong La-deposited species interaction. As La content in carriers increased Mo=O Raman stretching vibrations shifted to lower wave-numbers (949 to 935 cm −1 ) suggesting octahedral molybdates coordination change to tetrahedral. Although La at the lowest concentration (1 wt%) enhanced dibenzothiophene, HDS (~38% higher as to the Al 2 O 3 -supported formulation) desulfurization was significantly diminished at augmented content. Presence of hardly sulfidable tetrahedral Mo originated during impregnation at basic conditions in pores of La-modified carriers seemed to dictate observed behavior. Rare earth content in formulations enhanced selectivity to biphenyl.: J. Escobar acknowledges financial support from IMP (Y.00105) and SENER-CONACYTHidrocarburos (115086) fund.