Barium strontium titanate powders prepared by spray pyrolysis
Fecha
2005-09-15Registro en:
Materials Science and Engineering B-solid State Materials For Advanced Technology. Lausanne: Elsevier B.V. Sa, v. 122, n. 2, p. 140-144, 2005.
0921-5107
10.1016/j.mseb.2005.05.016
WOS:000231333600011
9128353103083394
Autor
University of Belgrade
Universidade Estadual Paulista (Unesp)
Universidade Federal de São Carlos (UFSCar)
Resumen
Ultasonic spray pyrolysis (SP) has been investigated for the production of the barium strontium titanate (BST) powders from the polymeric precursors. The processing parameters, such as flux of aerosol and temperature profile inside the furnace, were optimized to obtain single phase BST. The powders were characterized by the methods of X-ray diffraction analysis, SEM, EDS and TEM. The obtained powders were submicronic, consisting of spherical, polycrystalline particles, with internal nanocrystalline structure. Crystallite size of 10 nut, calculated using Rietveld refinement, is in a good agreement with results of HRTEM. (c) 2005 Elsevier B.V. All rights reserved.