Alternative Ni-Cr alloys applied in dentistry of two commercial brands for ceramometal restoration were evaluated. The alloys were analyzed in the commercial and after casting conditions using experimental techniques of metallography, X-ray diffraction, superficial hardness and density. The metalografics and X-ray diffraction analysis showed that, the alloys microstructure is marked with the presence of a solid solution having an ordered face- centred cubic structure, Ni-rich austenitic (y phase) matrix, and with fine precipitates particles of secondary phases. The Vicker hardness tests showed a decrease in hardness values of the studied alloys aer casting. The alloys density values, on the other hand, did not manifest changes.Com o propósito de contribuir com o estudo das ligas odontológicas alternativas, são apresentados os resultados de ensaios em duas marcas comerciais de ligas a base de Ni-Cr indicadas para trabalhos metalocerâmicos. As ligas foram analisadas na condições de venda ("condições comercial") e após fusão odontológica ("condição de fusio") utilizando técnicas experimentais de metalografia, difração de raio-X, dureza superficial e densidade. Os resultados da análise metalográfica e de difração de raio-X mostraram que a microestrutura das ligas e marcada pela formação de uma solução sólida rica em Ni, matriz austenitica com estrutura cúbica de fase centrada (fase y), sobre a qual se distribuem finos precipitados de fases secundarias. Os ensaios de microdureza Vickers demonstraram que as duas ligas sofrem um decréscimo dos valores de dureza superficial após submetidas à fusão. A densidade das ligas, no entanto, se mantem praticamente inalterada.