Dependence on the atmosphere of preparation of the luminescence of spark processed porous GaAs
Autor
ROJAS LÓPEZ, MARLON
Institución
Resumen
We report on the preparation of photoluminescent porous GaAs by the application of high voltage
spark discharges in atmospheres of pure oxygen, pure nitrogen, and in mixed N2:O2 ratios of 4:1
and 1:4. The spark-processed porous ~spp! samples were characterized by the observation of their
visible photoluminescence ~PL! when illuminated with UV monochromatic radiation. Some
differences are observed in the initial PL spectra of the spp-GaAs according to the atmosphere of
preparation under similar sparking and time conditions. The PL consists of two dominant bands, a
yellow-green band between ;2.2 and 2.6 eV and a blue-violet band, centered at 3.1 eV. Comparison
with Raman and PL results from As2O3 and As2O5 indicates that the PL in the spp-GaAs is
produced by the formation of these compounds by exposure to oxygen during the preparation. This
is reinforced by energy dispersive x-ray spectroscopy measurements that indicate that the spp-GaAs
is always oxidized, even when prepared under a nitrogen flow. The blue-UV emission at 3.1 eV
suggests that we cannot rule out confinement as a contributing mechanism for this PL. Raman
spectra indicate that for samples prepared in pure nitrogen, the resulting material consists of
amorphous As and GaAs, and the cubic form of As2O3 , arsenolite. PL and Raman indicate that
there exists an increasing degree of amorphization of the resultant material with the introduction of
nitrogen in the preparation atmosphere. © 2000 American Institute of Physics.