Novel cellulose/NbOPO 4.nH 2O hybrid material from sugarcane bagasse
Fecha
2011-02-01Registro en:
BioResources, v. 6, n. 1, p. 867-878, 2011.
1930-2126
WOS:000288944400055
2-s2.0-80054062813
2-s2.0-80054062813.pdf
3511534795805776
6119671014416126
Autor
Universidade Estadual Paulista (Unesp)
Universidade de São Paulo (USP)
Institución
Resumen
In recent years studies concerning the applications of lignocellulosic/ inorganic couples have resulted in the development of an interesting class of functional materials. In this work a cellulose/NbOPO 4.nH 2O hybrid using cellulose from surgacane bagasse was prepared and characterized in order to test for adsorption applications. The preparation process was conducted by carrying out metallic niobium dilution in hydrofluoric acid in the presence of nitric acid, then adding boric acid to form the complex and, finally, the cellulose sugar cane bagasse was added. Concentrated phosphoric acid was also inserted to precipitate hydrous niobium phosphate particles in the cellulose fiber. This material was characterized by X-ray diffractometry (XRD), thermogravimetry (TG/DTG), and scanning electronic microscopy (SEM) connected to an energy dispersive spectrophotometer (EDS). Results by SEM/EDS show that NbOPO 4.nH 2O was present in structure of the cellulose. During the preparation of the material, using boric acid it was observed that the formation of precipitate occurred in a shorter time than the material prepared without boric acid.