Effect of thermocycling aging on the flexural strength of feldspathic ceramic
Efeito da termociclagem na resistência flexural de uma cerâmica feldspática
Fecha
2018-01-01Registro en:
Brazilian Dental Science, v. 21, n. 3, p. 315-319, 2018.
2178-6011
10.14295/bds.2018.v21i3.1554
2-s2.0-85052292851
967916388665754
0000-0003-0586-4644
Autor
Universidade Estadual Paulista (Unesp)
Institución
Resumen
Objective: The aim of the study was to evaluate the effect of aging through different thermocycling protocols on the flexural strength of a feldspathic ceramic. Material and Methods: Fifty ceramic bars, Vitablock Mark II (VITA), with dimensions of 18X4X2mm were prepared. The bars were randomly distributed to the groups (n = 10), which were defined according to the number of thermal cycles (TCy): G0-no TCy; G500-500 cycles of TCy; G6000-6000 TCy; G10000-10000 TCy; G15000-15000 TCy. After aging, the specimens were subjected to the three point bending test in a universal testing machine (EMIC DL 1000), under 0.5mm/min speed and loading of 50kgf, until catastrophic failure. A sample of each group was evaluated for topographic morphology under Scanning Electron Microscopy. Results: For mechanical testing, the following mean values and standard deviation (MPa) were obtained: G0 (99.78 ± 5.07); G500 (101.64 ± 5.59); G6000 (98.13 ± 4.95); G10000 (91.77 ± 9.68); G15000 (101.51 ± 4.22). An analysis of variance by regression equation (p = 0.387) was performed, demonstrating a weak and non-significant correlation between flexural strength and number of thermal cycles. Conclusion: It can be concluded that aging in water solely by different numbers of temperature cycles did not influence on the flexural strength of a feldspathic ceramic.