A brief discussion on (pure mode I) fatigue crack growth rate data in 5HS weave fabric composites: Evaluation of empirical relations
Fecha
2016-03-01Registro en:
International Journal of Fatigue, v. 84, p. 97-103.
0142-1123
10.1016/j.ijfatigue.2015.11.019
2-s2.0-84949516950
2-s2.0-84949516950.pdf
2160957529151025
6119671014416126
Autor
Universidade Estadual Paulista (Unesp)
Aerospace Structures and Materials
Vila das Acácias
Institución
Resumen
A major concern in laminated composites for structural applications has been crack nucleation between plies and its propagation through the interface. A better comprehension of stable crack propagation may lead to more reliable predictions of the rate with which cracks grow in weave fabric laminated composites. To this aim, a number of empirical relationships proposed in the literature were studied for their applicability to satin weave fabric (5HS) composite with spread tows. In order to understand the fatigue delamination process, Double Cantilever Beam specimens were submitted to cyclic loading, and their respective da/dN vs strain energy release rate (SERR) data collected and correlated to these empirical relationships. Despite that the empirical or semi-empirical relations fit equally well to the data, the well-known Hartman-Schijve equation was adopted. This equation was properly modified according to the fracture surface investigation which had its fracture patterns qualitatively correlated with SERR parameters.