Surface characterization of polymers used in fabrication of interim prostheses after treatment with photopolymerized glaze
Fecha
2017-02-01Registro en:
Materials Science & Engineering C-materials For Biological Applications. Amsterdam: Elsevier Science Bv, v. 71, p. 755-763, 2017.
0928-4931
10.1016/j.msec.2016.10.059
WOS:000390967200089
WOS000390967200089.pdf
9719883814872582
Autor
Universidade Estadual Paulista (Unesp)
Institución
Resumen
The material used for interim prostheses fabrication must present excellent physical properties for greater longevity in the face of environmental conditions, which can occur in the oral cavity. The purpose of this study was to evaluate the effect of a photopolymerized glaze on the physical and mechanical properties of polymers used for the fabrication of interim prostheses, before and after thermocycling and immersion in staining solutions. One hundred samples of composite and acrylic resins were fabricated: Dencor chemically activated acrylic resin (CAAR) (n = 20) and heat-polymerized acrylic resin (HPAR) (n = 20), Charisma (n = 20), Structur (n = 20), and Protemp (n = 20). A mechanical polishing was performed on half of the samples, and a chemical polishing was performed on the remaining samples. Subsequently, all samples were submitted to thermocycling and immersion in coffee staining solution for 21 days. Analysis of color and microhardness, as well as atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy dispersive x-ray spectrometry (EDS) were performed. The data were submitted to repeated-measures analysis of variance (ANOVA), followed by the Tukey test (alpha = 0.05) and the Student t-test (alpha = 0.05). It was verified that the glaze decreased the chromatic alteration values, and increased the microhardness values of the samples, with the exception of the Charisma resin. The samples that did not receive chemical polishing had the greatest number of surface irregularities. This study concluded that the groups with glaze presented less color alteration. In addition, Charisma and Structur resins exhibited the greatest chromatic stability. As to the microhardness, the values were greater when the samples were treated with the glaze, with the exception of the Charisma group. (C) 2016 Elsevier B.V. All rights reserved.