Y2O3:Eu3+ (5 mol%) with Ag nanoparticles prepared by citrate precursor
Fecha
2010-09-01Registro en:
Journal of Solid State Chemistry. San Diego: Academic Press Inc. Elsevier B.V., v. 183, n. 9, p. 2110-2115, 2010.
0022-4596
10.1016/j.jssc.2010.07.010
WOS:000282139600030
4284809342546287
2034352556339501
2034352556339501
Autor
Universidade Estadual Paulista (Unesp)
Universidade Federal de Sergipe (UFS)
Institución
Resumen
Y2O3:Eu3+ (5 mol% Eu3+) and Y2O3:Eu3+ (5 mol% Eu3+) containing 1 mol% of Ag nanoparticles were prepared by heat treatment of a viscous resin obtained via citrate precursor. TEM and EDS analyses showed that Y2O3:Eu3+ (5 mol% Eu3+) is formed by nanoparticles with an average size of 12 nm, which increases to 30 nm when Ag is present because the effect of metal induced crystallization occurs. Ag nanoparticles with a size of 9 nm dispersed in Y2O3:Eu3+ (5 mol% Eu3+) were obtained and the surface plasmon effect on Ag nanoparticles was observed. The emission around 612 nm assigned to the Eu3+ (D-5(0) -> F-7(2)) transition enhanced when the Ag nanoparticles were present in the Y2O3:Eu3+ luminescent material. (C) 2010 Elsevier B.V. All rights reserved.