Chemical composition and phase identification of sodium titanate nanostructures grown from titania by hydrothermal processing
Fecha
2007Registro en:
Journal of Physics and Chemistry of Solids 68 (2007) 628–637
doi:10.1016/j.jpcs.2007.02.011
Autor
Zárate Aliaga, Ramón
Fuentes, S.
Wiff, Juan P.
Fuenzalida, V. M.
Cabrera, A. L.
Institución
Resumen
Fine titanium dioxide particles were hydrothermally treated in a sodium hydroxide aqueous solution. The treatment extended from 1
to 6 days leading to belt-like and wire-like structures of a metastable phase of sodium titanate, with typical widths and diameters between
8 and 40 nm, and lengths from 100nm to several micrometers. These conclusions are supported by X-ray photoelectron spectroscopy,
X-ray diffraction, Raman spectroscopy and high resolution transmission electron microscopy. The latter method revealed two set of
space fringes with characteristic distances of 0.29 and 0.34 nm. These distances could correspond to the lattice spacing of ½ 311 and
½ 111 planes in Na2Ti6O13 compounds. The nanomaterial was found to be stable up to temperatures as high as 200 or 400 C
depending on the reaction time and the concentration.