This study reports the statistical analysis of 7,308 tests performed to determine the effects of different types and contents of mineral additions, water/cement ratios, and axial compressive strength of binary and ternary concrete mixtures with mineral additions on microstructure and durability parameters. Simple and multiple linear regression analyses and analysis of variance indicated that porosity, combined water, and remaining calcium hydroxide have influenced microstructure, whereas carbonation, chloride penetration, and water absorption affected durability. Mineral addition content had the most significant influence, followed by water/cement ratio, addition type, and compressive strength. The statistical results confirm the beneficial effects of mineral additions on concrete properties, which is consistent with a large number of studies reported on the literature.Este trabalho apresenta por meio de análise estatística de 7308 ensaios a significância da influência do tipo e teor de adições minerais, relação água/materiais cimentícios e da resistência à compressão axial de misturas binárias e ternárias de concretos com adições minerais, sobre variáveis que se relacionam com a microestrutura e durabilidade. Por meio de regressões lineares simples e múltiplas e de análise de variância conclui-se que os parâmetros que influenciaram as variáveis dependentes da microestrutura e durabilidade, a partir das variáveis independentes que integraram os modelos gerais das regressões lineares múltiplas, o teor de adição mineral foi o que apresentou maior significância, seguido da relação água/materiais cimentícios, tipo de adição e, por último, resistência à compressão.