Synthesis and stimulated luminescence property of Zn(BO2)2:Tb3+
Fecha
2017-09Registro en:
Del Rosario, G. Cedillo; Cruz Zaragoza, Epifanio; Hipólito, M. García; Marcazzo, Salvador Julian; Hernández A., J. M.; et al.; Synthesis and stimulated luminescence property of Zn(BO2)2:Tb3+; Pergamon-Elsevier Science Ltd; Applied Radiation and Isotopes; 127; 9-2017; 103-108
0969-8043
CONICET Digital
CONICET
Autor
Del Rosario, G. Cedillo
Cruz Zaragoza, Epifanio
Hipólito, M. García
Marcazzo, Salvador Julian
Hernández A., J. M.
Murrieta S. H.
Resumen
Zinc borate, Zn(BO2)2, doped with different concentrations of terbium (0.5–8 mol%) was synthesized and polycrystalline samples were characterized by Scanning Electron Microscopy and X-Ray Diffraction. The Zn(BO2)2 was formed in the pure samples sintered at 750 and 800 °C which has the body centered cubic structure, and a ZnB4O7 primitive orthorhombic phase was present. The thermoluminescent intensity was dependents on the thermal treatment (250–500 °C) and also on the impurity concentration. The linear dose-response was obtained between 0.022–27.7 Gy and 0.5–50 Gy when the samples were exposed to beta and gamma radiation, respectively. The complex structure of the glow curves was analyzed by the Computerized Glow Curve Deconvolution method. The kinetics parameters were calculated assuming the general order kinetics model describing accurately the TL process. The glow curves of Tb3+-doped zinc borate phosphor were well deconvolved by six glow peaks. Zinc borate with 8 mol% of impurity concentration exhibited an intense radioluminescent emission. The radioluminescent spectra show their maximum bands at 370, 490, 545 and 700 nm related to the terbium ion in the zinc borate. These obtained results suggest that the terbium doped zinc borate is a promising phosphor for use in radiation dosimetry because of its high TL sensitivity to the ionizing radiation.