Magnetostriction of melt-spun Fe(85)Ga(15), Fe(78)Ni(7)Ga(15) and Fe(78)Co(7)Ga(15) stacked ribbon samples
Fecha
2010Registro en:
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, v.322, n.9/Dez, p.1605-1608, 2010
0304-8853
10.1016/j.jmmm.2009.06.008
Autor
BORMIO-NUNES, C.
TURTELLI, R. Sato
GROESSINGER, R.
MUELLER, H.
SASSIK, H.
Institución
Resumen
A set of stacked ribbon samples with the compositions Fe(85)Ga(15), Fe(78)Ni(7)Ga(15) and Fe(78)Co(7)Ga(15) were prepared. XRD on these ribbons show that the binary Fe(85)Ga(15) ribbon exhibits the disordered A2 structure where as the addition of Co and Ni leads to the appearance of an additional ordered DO(3) structure. A comparison of the ratio of the XRD-line intensities gave strong evidence of a (100) texture perpendicular to the ribbon surface. The optical studied microstructure supports these results because it shows a columnar grain growth parallel to the solidification direction-which is parallel to ribbon thickness. The highest magnetostriction was found for Fe(78)Ni(7)Ga(15) (370 ppm), while the Fe(78)Co(7)Ga(15) a smaller magnetostriction of 270 ppm was found. The enhancement of the magnetostriction is attributed to the (100) texture in these ribbons. (C) 2009 Elsevier B.V. All rights reserved.