The aim of this study was to compare the polymerization contraction stress of composites photoactivated by two light sources: quartz tungsten halogen light (QTH) and light emitting diode (LED). Glass rods were fabricated (5.0 mm X 5.0 cm) and one of the surfaces was air abraded with aluminum oxide. An adhesive was applied to this surface and photoactivated by LED. The glass rods were assembled to a Universal Testing machine (Instron - 5565) and the composite were applied to the lower rod using a manual instrument. The upper rod was placed closer, at 2 mm, and an extensometer was attached to the rods. The twenty composites were polymerized by either by QTH (N.=10) or LED (N.=10). Polymerization was carried out using two apparatuses positioned in opposite sides, which were simultaneously activated for 30 seconds. Contraction stress was analyzed twice: shortly after polymerization (t30s) and 30 minutes later (t30min). The contraction stress for all composites was higher at t30min than at t30s, regardless of the activation source. Z100 showed lower contraction stress values (P<0.05) compared to the other composites. Regarding to Charisma and TPH, the photoactivation source had no influence on contraction stress, except for Z100 at t30min. It was concluded that composite composition is the factor that most influence the polymerization contraction stress. 58 577-84
Ítems relacionados
Mostrando ítems relacionados por Título, autor o materia.
-
Comparativo de custos dos métodos construtivos: Light Steel Frame, Light Wood Frame e Concreto Armado com Alvenaria de Vedação
Moura, Breno Ribeio de; Barbosa, Diego Pires; Souza, Eduardo Henrique de; Oliveira, Guilherme Ducceschi de; Vieira, Patricia Talhas -
Estudo comparativo entre sistemas construtivos industrializados: Light Steel Frame e Light Wood Frame
Zehnder, Luan; Corrêa, Daiane Fernandes