Designed pendant chain covalently bonded to analogue of heulandite for removal of divalent toxic metals from aqueous solution: Thermodynamic and equilibrium study (Retracted article. See vol. 357, pg. 559, 2011)
Registro en:
Journal Of Colloid And Interface Science. Academic Press Inc Elsevier Science, v. 337, n. 1, n. 122, n. 130, 2009.
0021-9797
WOS:000268111800017
10.1016/j.jcis.2009.05.013
Autor
Guerra, DL
Viana, RR
Airoldi, C
Institución
Resumen
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) An analogue of heulandite was synthesized by using inorganic salts as a source for silicon and aluminum in the hydrothermal synthesis of the material. The resulting solid was modified by organofunctionalization with 1,4-bis(3-aminopropyl)piperazine and subsequent reaction with methylacrylate in a heterogeneous route. The original (HEU) and modified silicate (HEUAPPMA) samples were characterized by textural analysis, SEM, and nuclear magnetic nuclei of (29)Si and (13)C. The chemically modified silicate sample showed modification of its physical-chemical properties including specific area 459.0-978.8 m(2) g(-1). The ability of this material to remove nickel(II), cobalt(II), and copper(II) from aqueous solutions was followed by a series of adsorption isotherms adjusted to a Sips equation. The quick adsorption process reached the equilibrium before 10, 15, and 20 min for Cu(II), Ni(II), and Co(II), respectively, with maximum adsorptions at pH 4.0. Based on the capacity of adsorption of HEUAPPMA to interact with metal ions, the following results were obtained 12.9, 9.8, and 7.5 mmol g(-1) for Cu(II), Ni(II), and Co(II), respectively, reflecting a maximum adsorption order of Cu(II) > Ni(II) > Co(II). The energetic effects caused by metal cation adsorption were determined through calorimetric titrations. (C) 2009 Published by Elsevier Inc. 337 1 122 130 Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)