Artículos de revistas
Effect Of Replacing A Component Of A Self-etch Adhesive By Chlorhexidine On Bonding To Dentin
Brazilian Dental Journal. , v. 24, n. 4, p. 335 - 339, 2013.
di Hipolito V.
de Goes M.F.
The purpose of this study was to evaluate the effect of replacing a component of the self-etch adhesive Adper Scotchbond SE (liquid A + liquid B) by 2% chlorhexidine (CHX) on bond strength to dentin after 1 day, 3 months or 6 months of water storage. Eight human teeth were sectioned to expose a flat dentin surface and were then randomly assigned to 2 groups. In the control group, the dentin surfaces were treated with the adhesive according to the manufacturer's instructions. In the experimental group, liquid A was replaced by 2% CHX. Next, a 6-mm-high resin composite block was incrementally built on the bonded surfaces. The restored teeth were then sectioned to produce stickshaped specimens (cross-sectional area - 0.8 mm2). The microtensile bond strength (μTBS) was recorded, and the failure modes were assessed. Data were analyzed by two-way repeated measures ANOVA (α=0.05). Four additional teeth were processed in order to conduct a micromorphological analysis of the resin-dentin interface. The μTBS values did not significantly decrease after water storage in either the control or the experimental group, whose values did not differ significantly irrespective of storage time. The morphological aspect of the bonding interface appears not to have been affected by CHX. A higher incidence of cohesive failures within the adhesive and mixed failures (cohesive within adhesive and resin composite) was observed for both groups. It may be concluded that dentin pre-treatment with 2% CHX did not influence significantly the bonding performance of the evaluated adhesive.244335339Verma, R., Singh, U.P., Tyagi, S.P., Nagpal, R., Manuja, N., Long-term bonding effectiveness of simplified etch-and-rinse adhesives to dentin after different surface pre-treatments (2013) J Conserv Dent, 16, pp. 367-370Carrilho, M.R., Geraldeli, S., Tay, F., de Goes, M.F., Carvalho, R.M., Tjaderhane, L., In vivo preservation of the hybrid layer by chlorhexidine (2007) J Dent Res, 86, pp. 529-533Ito, S., Hoshino, T., Iijima, M., Tsukamoto, N., Pashley, D.H., Saito, T., Water sorption/solubility of self-etching dentin bonding agents (2010) Dent Mater, 26, pp. 617-626Hosaka, K., Nakajima, M., Takahashi, M., Itoh, S., Ikeda, M., Tagami, J., Relationship between mechanical properties of one-step self-etch adhesives and water sorption (2010) Dent Mater, 26, pp. 360-367Hashimoto, M., A review--micromorphological evidence of degradation in resin-dentin bonds and potential preventional solutions (2010) J Biomed Mater Res B Appl Biomater, 92, pp. 268-280Hebling, J., Pashley, D.H., Tjaderhane, L., Tay, F.R., Chlorhexidine arrests subclinical degradation of dentin hybrid layers in vivo (2005) J Dent Res, 84, pp. 741-746Van Meerbeek, B., Yoshihara, K., Yoshida, Y., Mine, A., De Munck, J., Van Landuyt, K.L., State of the art of self-etch adhesives (2011) Dent Mater, 27, pp. 17-28Van Landuyt, K.L., Snauwaert, J., De Munck, J., Peumans, M., Yoshida, Y., Poitevin, A., Systematic review of the chemical composition of contemporary dental adhesives (2007) Biomaterials, 28, pp. 3757-3785Tay, F.R., King, N.M., Chan, K.M., Pashley, D.H., How can nanoleakage occur in self-etching adhesive systems that demineralize and infiltrate simultaneously? (2002) J Adhes Dent, 4, pp. 255-269Carvalho, R.M., Chersoni, S., Frankenberger, R., Pashley, D.H., Prati, C., Tay, F.R., A challenge to the conventional wisdom that simultaneous etching and resin infiltration always occurs in self-etch adhesives (2005) Biomaterials, 26, pp. 1035-1042Salz, U., Zimmermann, J., Zeuner, F., Moszner, N., Hydrolytic stability of self-etching adhesive systems (2005) J Adhes Dent, 7, pp. 107-116Inokoshi, S., Hosoda, H., Harnirattisai, C., Shimada, Y., Interfacial structure between dentin and seven dentin bonding systems revealed using argon ion beam etching (1993) Oper Dent, 18, pp. 8-16Vaz, R.R., Hipolito, V.D., D'Alpino, P.H., Goes, M.F., Bond strength and interfacial micromorphology of etch-and-rinse and self-adhesive resin cements to dentin (2012) J Prosthodont, 21, pp. 101-111Lenzi, T.L., Tedesco, T.K., Soares, F.Z., Loguercio, A.D., de Rocha, R.O., Chlorhexidine does not increase immediate bond strength of etchand-rinse adhesive to caries-affected dentin of primary and permanent teeth (2012) Braz Dent J, 23, pp. 438-442De Munck, J., Van den Steen, P.E., Mine, A., Van Landuyt, K.L., Poitevin, A., Opdenakker, G., Inhibition of enzymatic degradation of adhesivedentin interfaces (2009) J Dent Res, 88, pp. 1101-1106Yiu, C.K., King, N.M., Pashley, D.H., Suh, B.I., Carvalho, R.M., Carrilho, M.R., Effect of resin hydrophilicity and water storage on resin strength (2004) Biomaterials, 25, pp. 5789-5796do Amaral, R.C., Stanislawczuk, R., Zander-Grande, C., Michel, M.D., Reis, A., Loguercio, A.D., Active application improves the bonding performance of self-etch adhesives to dentin (2009) J Dent, 37, pp. 82-90Albuquerque, M., Pegoraro, M., Mattei, G., Reis, A., Loguercio, A.D., Effect of double-application or the application of a hydrophobic layer for improved efficacy of one-step self-etch systems in enamel and dentin (2008) Oper Dent, 33, pp. 564-570Felizardo, K.R., Lemos, L.V., de Carvalho, R.V., Gonini Jr., A., Lopes, M.B., Moura, S.K., Bond strength of HEMA-containing versus HEMA-free selfetch adhesive systems to dentin (2011) Braz Dent J, 22, pp. 468-472De Munck, J., Mine, A., Van den Steen, P.E., Van Landuyt, K.L., Poitevin, A., Opdenakker, G., Enzymatic degradation of adhesive-dentin interfaces produced by mild self-etch adhesives (2010) Eur J Oral Sci, 118, pp. 494-501Mine, A., De Munck, J., Cardoso, M.V., Van Landuyt, K.L., Poitevin, A., Kuboki, T., Bonding effectiveness of two contemporary self-etch adhesives to enamel and dentin (2009) J Dent, 37, pp. 872-883Sarr, M., Kane, A.W., Vreven, J., Mine, A., Van Landuyt, K.L., Peumans, M., Microtensile bond strength and interfacial characterization of 11 contemporary adhesives bonded to bur-cut dentin (2010) Oper Dent, 35, pp. 94-104Ferracane, J.L., Berge, H.X., Condon, J.R., In vitro aging of dental composites in water--effect of degree of conversion, filler volume, and filler/ matrix coupling (1998) J Biomed Mater Res, 42, pp. 465-472Skovron, L., Kogeo, D., Gordillo, L.A., Meier, M.M., Gomes, O.M., Reis, A., Effects of immersion time and frequency of water exchange on durability of etch-and-rinse adhesive (2010) J Biomed Mater Res B Appl Biomater, 95, pp. 339-346Van Meerbeek, B., Peumans, M., Poitevin, A., Mine, A., Van Ende, A., Neves, A., Relationship between bond-strength tests and clinical outcomes (2010) Dent Mater, 26, pp. e100-e121