Singular Effect Of Crystallite Size On The Charge Carrier Generation Andphotocatalytic Activity Of Nano-tio2
Registro en:
Applied Surface Science. Elsevier, v. 319, n. 1, p. 151 - 157, 2014.
1694332
10.1016/j.apsusc.2014.06.071
2-s2.0-84922917287
Autor
Strauss M.
Pastorello M.
Sigoli F.A.
De Souza E Silva J.M.
Mazali I.O.
Institución
Resumen
Photocatalytic processes on nanometric titanium oxide have been extensively studied from the stand-point of solar energy utilization and remediation of water and gas streams polluted with organicmolecules. It is accepted that TiO2crystallite size and crystalline phase are among the parameters involvedin the control of the photocatalytic activity. However, while changing the catalyst nanoparticle size, otherattributes important to assess photocatalytic activity may be modified, making thus difficult to define towhich extension the photoactivity changes are related only to size differences. Therefore, aiming at study-ing exclusively the size effect and the parameters directly related to size on the photocatalytic activity ofnanometric TiO2, in this work it was explored a method to synthesize TiO2nanoparticles with controlledsize, highly similar morphology and comparable phase and degree of crystallinity. A set composed offour samples of nano-TiO2loaded porous Vycor glass, each sample having a specific TiO2nanoparticlesize, was tested on the photoactivated process of depollution of solutions of salicylic acid and methyleneblue. The photocatalytic activity observed for the organic compounds tested was inversely proportionalto the TiO2nanoparticle size. An opposite tendency was observed for the generation of OH radicals dur-ing photocatalyst illumination, as more radicals are formed on the material containing the larger TiO2nanoparticles. Results of this study suggest that photocatalytic activity of nano-TiO2is less favored bythe enhanced light absorption response and the higher generation of oxidative species observed for thelarger nanoparticles. Better catalysts were obtained when nano-TiO2exhibited high surface-to-volumeratio and had small recombination volumes, which respectively favors pollutant adsorption-desorptionon catalyst surface and reduce the number of recombined charge carriers. 319 1 151 157 Mohamed, H.H., Bahnemann, D.W., The role of electron transfer in photocata-lysis: Fact and fictions (2012) Appl. Catal. B-Environ, 128, p. 91 Pelaez, M., Nolan, N.T., Pillai, S.C., Seery, M.K., Falaras, P., Kontos, A.G., Dunlop, P.S.M., Dionysiou, D.D., A review on the visible light active titanium dioxide photo-catalysts for environmental applications (2012) Appl. Catal. B-Environ, 125, p. 331 Teh, C.M., Mohamed, A.R., Roles of titanium dioxide and ion-doped titaniumdioxide on photocatalytic degradation of organic pollutants (phenolic com-pounds and dyes) in aqueous solutions: A review (2011) J. Alloy. Compd, 509, p. 1648 Chong, M.N., Jin, B., Chow, C.W.K., Saint, C., Recent developments in photocatalyticwater treatment technology: A review (2010) Water Res, 44, p. 2997 Zhang, J., Xu, Q., Feng, Z., Li, M., Li, C., Importance of the relationship betweensurface phases and photocatalytic activity of TiO2 (2008) Angew. Chem. Int. Ed, 47, p. 1766 Joo, J.B., Zhang, Q., Dahl, M., Lee, I., Goebl, J., Zaera, F., Yi, Y., Control of the nanoscalecrystallinity in mesoporous TiO2shells for enhanced photocatalytic activity (2012) Energ. Environ. Sci, 5, p. 6321 Yu, J., Wang, G., Cheng, B., Zhou, M., Effects of hydrothermal temperature and timeon the photocatalytic activity and microstructures of bimodal mesoporous TiO2powders (2007) Appl. Catal. B-Environ, 69, p. 171 Yu, J.G., Su, Y.R., Cheng, B., Template-free fabrication and enhanced photocat-alytic activity of hierarchical macro-/mesoporous titania (2007) Adv. Funct. Mater, 17, p. 1984 Yang, H.G., Liu, G., Qiao, S.Z., Sun, C.H., Jin, Y.G., Smith, S.C., Zou, J., Lu, G.Q., Solvothermal synthesis and photoreactivity of anatase TiO2nanosheetswith dominant { 001} facets (2009) J. Am. Chem. Soc, 131, p. 4078 Ariga, H., Taniike, T., Morikawa, H., Tada, M., Min, B.K., Watanabe, K., Matsumoto, Y., Iwasawa, Y., Surface-mediated visible-light photo-oxidationon pure TiO2 001) (2009) J. Am. Chem. Soc, 131, p. 14670 Kong, M., Li, Y., Chen, X., Tian, T., Fang, P., Zheng, F., Zhao, X., Tuning the relativeconcentration ratio of bulk defects to surface defects in TiO2nanocrystals leadsto high photocatalytic efficiency (2011) J. Am. Chem. Soc, 133, p. 16414 Strauss, M., Maroneze, C.M., De Souza, S.J.M., Sigoli, F.A., Gushikem, Y., Mazali, I.O., Annealing temperature effects on sol-gel nanostructured mesoporousTiO2/SiO2and its photocatalytic activity (2011) Mater. Chem. Phys, 126, p. 188 Carneiro, J.T., Savenije, T.J., Moulijn, J.A., Mul, G., Toward a physically soundstructure-activity relationship of TiO2-based photocatalysts (2010) J. Phys. Chem C, 114, p. 327 Zhang, J., Xiao, X., Nan, J., Hydrothermal-hydrolysis synthesis and photocatalyticproperties of nano-TiO2/SiO2with an adjustable crystalline structure (2010) J. Hazard. Mater, 176, p. 617 Yu, Y., Xu, D., Single-crystalline TiO2nanorods: Highly active and easily recycledphotocatalysts (2007) Appl. Catal. B-Environ, 73, p. 166 Shan, A.Y., Mohd, T.I., Rashid, G.S.A., Immobilisation of titanium dioxide ontosupporting materials in heterogeneous photocatalysis: A review (2010) Appl. Catal. A-Gen, 389, p. 1 Vest, R.W., Singaram, S., Synthesis of metallo-organic compounds for MOD pow-ders and films (1985) Mater. Res. Soc. Symp. Proc, 35, p. 60 Shifu, C., Xiaoling, Y., Huaye, Z., Wei, L., Preparation and photocatalytic activityevaluation of composite Fe - TiO2/ TiO2photocatalyst (2010) J. Electrochem. Soc, 157, p. K96 Li, D., Chen, Z., Chen, Y., Li, W., Huang, H., He, Y., Fu, X., A new route for degradationof volatile organic compounds under visible light: Using the bifunctional pho-tocatalyst Pt/TiO2-xNxin H2-O2atmosphere (2008) Environ. Sci. Technol, 42, p. 2130 Mazali, I.O., Souza Filho, A.G., Viana, B.C., Mendes Filho, J., Alves, O.L., Size-controllable synthesis of nanosized-TiO2anatase using porous Vycor glass astemplate (2006) J. Nanopart. Res, 8, p. 141 Correa, D.N., De Souza, S.J.M., Santos, E.B., Sigoli, F.A., Souza, F.A.G., Mazali, I.O., TiO2- and CeO2-based biphasic core-shell nanoparticles with tunablecore sizes and shell thicknesses (2011) J. Phys. Chem C, 115, p. 10380 Richter, H., Wang, Z.P., Ley, L., The one phonon Raman spectrum in microcrys-talline silicon (1981) Solid State Commun, 39, p. 625 Rouquerol, F., Rouquerol, J., Sing, K.S.W., (1999) Adsorption by Powders and PorousSolids, , Academic Press San Diego Lowell, S., Shields, J.E., Thomas, M.A., Thommes, M., (2006) Characterization of PorousSolids and Powders: Surface Area, , Pore Size and Density Springer, Dordrecht Thommes, M., Smarsly, B., Groenewolt, M., Ravikovitch, P.I., Neimark, A.V., Adsorp-tion hysteresis of nitrogen and argon in pore networks and characterization ofnovel micro- and mesoporous silicas (2006) Langmuir, 22, p. 756 Toyoda, T., Tsuboya, I., Apparent band-gap energies of mixed TiO2nanocrystalswith anatase and rutile structures characterized with photoacoustic spec-troscopy (2003) Rev. Sci. Instrum, 74, p. 782 Enright, B., Fitzmaurice, D., Spectroscopic determination of electron and holeeffective masses in a nanocrystalline semiconductor film (1996) J. Phys. Chem, 100, p. 1027 De Souza, S.J.M., Pastorello, M., Strauss, M., Maroneze, C.M., Sigoli, F.A., Gushikem, Y., Mazali, I.O., Size controlled synthesis of highly dispersedanatase/rutile nanoparticles with photocatalytic activity toward salicylic aciddegradation (2012) RSC Adv, 2, p. 5390 Zumeta, I., Daz, D., Santiago, P., Synthesis of TiO2nanoparticles with narrow sizedistribution and their evaluation in the photocatalytic oxidative degradationof bis(4-nitrophenyl) phosphate (2010) J. Phys. Chem C, 114, p. 11381 Karvaly, B., Hevesi, I., Investigations on diffuse reflectance spectra of V2O5pow-der (1971) Z. Naturforsch A, 26, p. 245 Kongkanand, A., Tvrdy, K., Takechi, K., Kuno, M., Kamat, P.V., Quantum dot solarcells. Tuning photoresponse through size and shape control of CdSe-TiO2archi-tecture (2008) J. Am. Chem. Soc, 130, p. 4007 Jacobsson, T.J., Edvinsson, T., Absorption and fluorescence spectroscopy of grow-ing ZnO quantum dots: Size and band gap correlation and evidence of mobiletrap states (2011) Inorg. Chem, 50, p. 9578 Hachiya, S., Onishi, Y., Shen, Q., Toyoda, T., Dependences of the optical absorptionand photovoltaic properties of CdS quantum dot-sensitized solar cells on theCdS quantum dot adsorption time (2011) J. Appl. Phys, 110, p. 054319 Xiang, Q., Yu, J., Wong, P.K., Quantitative characterization of hydroxyl radicalsproduced by various photocatalysts (2011) J. Colloid Interface Sci, 357, p. 163 Ismail, A.A., Bahnemann, D.W., Mesoporous titania photocatalysts: Preparation, characterization and reaction mechanisms, J (2011) Mater. Chem, 21, p. 11686 Matilainen, A., Sillanp, M., Removal of natural organic matter from drinkingwater by advanced oxidation processes (2010) Chemosphere, 80, p. 351