Mechanical Instability Of Anodic Films On Aluminum
Registro en:
Langmuir. , v. 8, n. 9, p. 2098 - 2100, 1992.
7437463
2-s2.0-0026924350
Autor
Teschke O.
Kleinke M.U.
Galembeck F.
Institución
Resumen
The mechanical instability of anodic oxide films formed on aluminum rod surfaces was analyzed using Euler's method applied to thin cylindrical shells under compressive forces. The ratio Δγ/E between the aluminum oxide/aluminum work of adhesion per unit area Δγ and the bulk modulus E of the film-forming aluminum (hydrous) oxide was determined for coating films formed under various anodic currents. © 1992 American Chemical Society. 8 9 2098 2100