Evaluation Of The Shear Bond Strength Of The Right-on Composite Under Different Enamel Conditions [avaliação Da Resistência Ao Cisalhamento Do Compósito Right-on Em Diferentes Condições De Esmalte]
Registro en:
Revista Dental Press De Ortodontia E Ortopedia Facial. , v. 13, n. 3, p. 60 - 65, 2008.
14155419
2-s2.0-49249128998
Autor
Pithon M.M.
Bernardes L.A.A.
de Oliveira Ruellas A.C.
Romano F.L.
Institución
Resumen
Objective: To evaluate the shear bond strength of metallic brackets bonded with Right-On composite under different enamel conditions. Materials and methods: Forty-five bovine permanent lower incisors were used, and were divided into three groups (n = 15). For group 1 (control), the bonding procedures were performed by using Transbond XT according to the manufacturer's recommendations, that is 37% phosphoric acid etching, washing, drying, application of primer XT and, finally, the bonding procedure itself. For the other two groups, the brackets were bonded by using the Right-On composite. The bonding procedures for group 2 were performed according to the manufacturer's recommendations, that is 37% phosphoric acid etching, application of the composite activation liquid, both on the etched surface and the bracket's base, and insertion of the composite on the bracket's base and bracket positioning. In group 3, the dental surface was etched by using Transbond Plus Self-Etching Primer, and the composite activator liquid was applied on the bracket's base only. Following the bonding procedures, the shear bond strength test was performed by using an Instron machine at the speed of 0.5mm/min. for mechanical tests. Results and conclusion: Results showed no statistical differences between groups 1 and 2 (p > 0.05). However, both groups were statistically superior to group 3 (p < 0.05). A greater number of fractures on the bracket/composite interface was evidenced by the ARI results. 13 3 60 65 ARTUN, J., BERGLAND, S., Clinical trials with crystal growth conditioning as an alternative to acid-etch enamel pretreatment (1984) Am. J. Orthod, 85 (4), pp. 333-340. , St. Louis, v, Apr BISHARA, S.E., Evaluation of a new light-cured orthodontic bonding adhesive (1998) Am. J. Orthod. Dentofacial Orthop, 114 (1), pp. 80-87. , St. Louis, v, July BISHARA, S.E., Effect of an acidic primer on shear bond strength of orthodontic brackets (1998) Am. J. Orthod. Dentofacial Orthop, 114 (3), pp. 243-247. , St. Louis, v, Sept BISHARA, S.E., Effect of time on the shear bond strength of glass ionomer and composite orthodontic adhesives (1999) Am. J. Orthod. Dentofacial Orthop, 116 (6), pp. 616-620. , St. Louis, v, Dec BOYD, R.L., Periodontal considerations in the use of bans or donds on molars in adolescents and adults (1982) Angle Orthod, 62 (3), pp. 117-120. , Appleton, v, May BUONOCORE, M.G.A., Alexandria (1955), 34 (6), pp. 849-853. , A simple method of increase the adhesion of acrylic filling materials to enamel surfaces. J. Dent. Res, DecBUONOCORE, M.G., Retrospections on bonding (1981) Dent. Clin. North Am, 25 (2), pp. 242-255. , Philadelphia, v, Apr DELPORT, A., GROEBLER, S.R., A laboratory evaluation of the tensile bond of strength of some orthodontic bonding resins to enamel (1988) Am. J. Orthod. Dentofacial Orthop, 93 (2), pp. 133-137. , St. Louis, v, Feb GORELIK, L., Bonding metal brackets with a self-polymerizing sealant composite: A 12 month assessment (1977) Am. J. Orthod, 75 (5), pp. 542-553. , St. Louis, v, May HOBSON, R.S., LEDVINKA, J., MEECHAN, J.G., The effect of moisture and blood contamination on bond strength of a new orthodontic bonding material (2001) Am. J. Orthod. Dentofacial Orthop, 120 (1), pp. 54-57. , St. Louis, v, July IANNI FILHO, D. et al. Avaliação in vitro da força de adesão de materiais de colagem em Ortodontia: ensaios mecânicos de cisalhamento. Rev. Dental Press Ortodon. Ortop. Facial, Maringá, v. 9, n. 1, p. 39-48, jan./fev. 2004LITTLEWOOD, S.J., Investigation of a hydrophilic primer for orthodontic bonding: An in vitro study (2000) J. Orthod, 27 (2), pp. 181-186. , London, v, May/Aug NORDENVALL, K.J., BRANSTRON, M., MALMGREN, T., The effect of various pretreatment methods of the enamel in bonding procedures (1978) Am. J. Orthod, 74 (4), pp. 522-530. , St. Louis, v, Apr PASCOTO, R.C., (1999) Avaliação das propriedades anticariogênicas do cimento de ionômero de vidro utilizado na fixação de bráquetes ortodônticos: Estudo in vitro. 1999, , Tese Doutorado, Faculdade de Odontologia de Bauru, Universidade de São Paulo, Bauru ROMANO, F. L. RUELLAS, A. C. O. Estudo comparativo in vitro da resistência ao cisalhamento da colagem e do índice de remanescente resinoso entre os compósitos concise e superbond. Rev. Dental Press Ortodon. Ortop. Facial, Maringá, v. 8, n. 1, p. 69-75, jan./fev. 2003SADLER, J.F., A survey of some commercial adhesives: Their possible application in clinical Orthodontics (1958) Am. J. Orthod, 44 (1), pp. 65-69. , St. Louis, v, Jan SCHANEVELDT, S., FOLEY, T.F., Bond strength comparison of moisture-insensitive primers (2002) Am. J. Orthod. Dentofacial Orthop, 122 (3), pp. 267-273. , St. Louis, v, Sept SUNNA, S., ROCK, An, W.P., ex vivo investigation into the bond strength of orthodontic brackets and adhesive systems (1999) Br. J. Orthod, 26 (4), pp. 47-50. , Oxford, v WILLEMS, G., CARELS, C.E.L., VERBEKET, G., In vitro peel/shear bond strength of orthodontic adhesives (1997) J. Dent, 25 (3-4), pp. 263-270. , Bristol, v ZACHRISSON, B. U. Bonding in Orthodontic. In: GRABER, T. M. WAIN, B. F. Orthodontic current principle and technique. St. Louis: C. V. Mosby, 1985. p. 485-563