Effects Of Liquid Core Reduction During Solidification Of Pb2.5wt%sb Thin Slabs
Registro en:
0878499911; 9780878499915
Materials Science Forum. , v. 508, n. , p. 379 - 384, 2006.
2555476
10.4028/0-87849-991-1.379
2-s2.0-35348905447
Autor
Peralta J.L.
Santos R.G.
Institución
Resumen
The influence of thickness reduction during solidification of Pb2.5wt%Sb thin slabs in the microstructure was experimentally analyzed using a physical simulator consisted of a water cooled mould with a moveable sidewall, driven by a hydraulic piston, to squeeze the liquid core during the solidification. Experiments were carried out in order to obtain slabs without thickness reduction and with thickness reduction of about 20% and 40%. The microstructures are revealed in order to analyze the influence of the thickness reduction applied in the formation of central equiaxial structure and in the secondary dendrite arm spacing. From the results it was observed that increasing the thickness reduction increases the extension of the equiaxial structure. 508
379 384 Wünnenberg, K., Schwerdtfeger, K., (1995) I&SM, p. 25 Gottardi, R., Nannini, L., Martegani, A.D., (1992) Metallurgical Plant and Technology International, 3, p. 46 Birat, J.P., (1998) La Revue de Metallurgie-CIT, p. 1387 Park, J.S., Ajmal, M., Priestner, R., (2000) ISIJ International, 40, p. 380 Kothe, D., (1995) Steelmaking Conf. Proc, p. 23 El-Gammal, T., (1992) Proc. Symp. Continuous Casting Res, p. 323. , Egypt Kaspar, R., Flüß, P., (1991) steel Res, 62, p. 501 Essadiqi, E., (1998) 39 MWSP Conference Proceeding, p. 883 Priestner, R., Zhou, C., (1995) Ironmaking and Steelmaking, 22, p. 326 Santos, R.G., (2001) Proceedings of International Conference on Advanced Materials Processing Technologies, 1, p. 9