This work aims the characterization of AES, a graft copolymer based on poly(styrene-co-acrylonitrile), SAN, and poly(etyhlene-co-propylene-co-diene), EPDM. AES was submitted to selective extraction of its components: free SAN, EPDM chains and the graft copolymer EPDM-g-SAN. AES and its fractions were characterized by infrared spectroscopy, elemental analysis, differential scanning calorimetry, 13C and ¹H nuclear magnetic resonance. The AES has 65 wt % of EPDM-g-SAN, 13 wt % of free EPDM and 22 wt % of free SAN. EPDM has 69.8 wt % of ethylene, 26.5 wt % of propylene and 4.6 wt % of diene, 2-ethylidene-5-norbonene ENB. SAN presents acrylonitrile/styrene mass ratio of 28/72 and a random distribution of acrylonitrile and styrene comonomers. These results are in agreement with the composition reported by the AES supplier, indicating that the proposed methodology is adequate.O objetivo deste trabalho é a caracterização do AES, um copolímero de enxertia de poli(estireno-co-acrilonitrila), SAN, em poli(etileno-co-propileno-co-dieno), EPDM. Para tanto, o AES foi submetido à extração seletiva de seus componentes: o SAN livre, o EDPM livre, e o copolímero de enxertia EPDM-g-SAN. O AES e suas frações foram caracterizados por espectroscopia de infravermelho, análise elementar, calorimetria diferencial de varredura e ressonância magnética nuclear, RMN¹H e RMN13C. O AES analisado apresenta a seguinte composição em massa: 65% de EPDM-g-SAN, 13% de EPDM livre e 22% de SAN livre. O EPDM apresenta 69,8% em massa de etileno, 26,5% em massa de propileno e 4,6% em massa do dieno, 2-etilideno-5-norboneno, ENB. O SAN apresenta razão em massa acrilonitrila/estireno de 28/72 e distribuição randômica de comonômeros de estireno e acrilonitrila. Estes resultados são concordantes com a composição do AES fornecida pelo fabricante, indicando que a metodologia proposta é adequada.158164Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)