Plates of the copolymer poly (lactide-co-glycolide) acid have been produced and used as implants that degrade and are absorbed by the organism. Implants that can be absorbed are advantageous in comparison with metallic implants. In this work, plates of the blend poly (lactide- co- glycolide) acid/ poly lactic acid (PLGA/ PLLA) were made and characterized during their in vitro degradation process. It was found that blends are immiscible and that their thermal stability increases with the proportion of PLLA in the blend. The crystallinity degree also increases with the proportion of PLLA in the sample and with degradation time. Besides, it was verified that PLGA is degraded quickly and its presence and amount modifies clearly the morphology of the blends.Placas de copolímero de poli(ácido lactico-co-glicólico) têm sido produzidas e usadas como implantes que degradam e são absorvidos pelo organismo. Implantes que podem ser absorvidos apresentam vantagens em relação aos implantes metálicos. Nesse trabalho, foram obtidas placas a partir de blendas de poli(ácido lactico-co-glicólico)/ poli(ácido lático), (PLGA/PLLA) e caracterizadas durante o processo de degradação in vitro. Verificou-se que as blendas são imiscíveis e a estabilidade térmica das mesmas aumenta com a proporção de PLLA. O grau de cristalinidade também aumenta com a proporção de PLLA na amostra e com o tempo de degradação. Além disso, verificou-se que o PLGA degrada rapidamente e sua presença e quantidade modifica nitidamente a morfologia das blendas.3644Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)