A water-soluble polymer prepared by sol-gel process, 3-n-propyl-1-azonia-4-azabicyclo[2.2.2]octane silsesquioxane chloride, was adsorbed on alumina surface. This polymer-coated alumina was able to effectively immobilize cobalt(II) tetrasulfonated phthalocyanine complexes as counter ions. Cobalt phthalocyanine immobilized in this way is well and tightly adsorbed on Al2O3/3-n-propyl-1-azonia-4-azabicyclo[2.2.2]octane silsesquioxane chloride surface. Furthermore, when incorporated to a carbon paste electrode showed a good electrocatalytic response toward the acid oxalic oxidation, making it a suitable electrode material. A linear relationship (r = 0.998) between the current responses obtained by chronoamperometric measurements and the oxalic acid concentration in the range of 7.4 × 10-5 - 9.1 × 10-4 mol L-1 was observed. A detection limit of 18 µmol L-1 was also determined.Um polímero solúvel em água, preparado pelo método sol-gel e designado cloreto de 3-n-propil-1-azonia-4-azabiciclo[2.2.2]octano silsesquioxano, foi adsorvido sobre a superfície da alumina. Essa alumina recoberta com o polímero foi capaz de imobilizar efetivamente complexos de ftalocianina tetrassulfonada metalada com Co(II) como contra-íons. A ftalocianina de cobalto imobilizada dessa forma fica fortemente aderida sobre a superfície do cloreto de Al2O3/3-n-propil-1-azonia-4-azabiciclo[2.2.2]octano silsesquioxano. Além disso, quando incorporada a um eletrodo de pasta de carbono mostra uma boa resposta eletrocatalítica para a oxidação de ácido oxálico. Foi obtida uma relação linear (r = 0,998) para o gráfico de correntes de resposta obtidas por cronoamperometria e a concentração de ácido oxálico na faixa de 7.4 ×10-5 a 9.1 × 10-4 mol L-1. O limite de detecção determinado foi igual a 18 µmol L-1.755761Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)