The shape recovery properties of an Fe-Mn-Si-Cr-Ni-Co based alloy were studied using compression tests. Analyzed were the elastic recovery (Er), shape recovery (Sr) and total shape recovery (T SR = Er + Sr) measurements as a function of training cycles. The results indicated that 3.3 was the best ratio between height (h o = 20 mm) and diameter (φo = 6 mm) to obtain a homogeneous deformation and defined loading curves. A major contribution of T SR was attributed to shape recovery. In the last training cycle, a T SR = 90 % was obtained, where 25% was attributed to Er.As propriedades de recuperação de forma da liga à base de Fe-Mn-Si-Cr-Ni-Co foram estudadas usando ensaio de compressão. Foram analisadas medidas de recuperação elástica (Re), recuperação de forma (Rf) e recuperação de forma total (R T = Re + Rf) em função do número de ciclos de treinamento. Os resultados indicaram que 3,3 foi a melhor razão entre altura (h o = 20 mm) e diâmetro (φo = 6 mm) para se conseguirem uma deformação homogênea e curvas de carregamento bem definidas. A maior contribuição para a R T foi atribuída à recuperação de forma. No último ciclo de treinamento, foi obtida uma R T = 90%, sendo 25% atribuída a Re.493499Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)