The aim of this work was to study the influence of Ni additions on the mechanical properties of Fe-Cr alloys. For this purpose, alloys were prepared with an 18%Cr-0.01%C-0.2%Si-0.4%Mn base composition and variable Ni content (0, 10, 20, 40 and 60 weight %). The alloys were characterized by X-Ray diffraction and thermal analyses. Their hardness was determined before and after cold deformation. Tension tests were carried out at room temperature and 350ºC to verify the effect of temperature on the mechanical behavior of the alloys. The mechanical characterization aim was to use these figures to correlate mechanical properties and machinability (results originating from a parallel study).O objetivo desse trabalho é estudar a influência de adições de níquel sobre as propriedades mecânicas de ligas Fe-Cr. Para atender a esse propósito, foram preparadas diversas ligas com a composição básica 18%Cr - 0,01%C - 0,2%Si - 0,4%Mn, variando-se o teor de níquel (0, 10, 20, 40 e 60 % em peso). A caracterização das ligas foi feita por difração de raios X e análise térmica. Foi determinada a dureza das ligas no estado como recebido e após a imposição de deformação a frio. Foram realizados ensaios de tração à temperatura ambiente e a 350ºC, para verificar o efeito da temperatura sobre o comportamento mecânico das mesmas. O objetivo da caracterização mecânica das ligas é o de associar as propriedades mecânicas com as propriedades de usinabilidade, obtidas em estudo que está sendo desenvolvido em paralelo.149154Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)