Influence of baking on the photoluminescence spectra of in11x xgaxasyp11y solid solutions grown on inp substrates

dc.creatorANDA , F. DE
dc.creatorGORBATCHEV A., YU
dc.creatorMISHURNYI , V.A.
dc.creatorNIETO NAVARRO, J.
dc.date2009-10-05
dc.date.accessioned2018-03-16T15:45:02Z
dc.date.available2018-03-16T15:45:02Z
dc.identifierhttp://ojs.unam.mx/index.php/rmf/article/view/13981
dc.identifier.urihttp://repositorioslatinoamericanos.uchile.cl/handle/2250/1202147
dc.descriptionSE HA ESTUDIADO LA INFLUENCIA DE DIFERENTES TRATAMIENTOS TÉRMICOS SOBRE LOS ESPECTROS DE FOTOLUMINISCENCIA DE CAPAS EPITAXIALES DE IN1-XGAXASYP1-Y CON DIFERENTES COMPOSICIONES, CRECIDAS SOBRE SUSTRATOS DE INP, MEDIANTE LA TÉCNICA DE EPITAXIA EN FASE LIQUIDA. EL ESPECTRO DE FOTOLUMINISCENCIA DE SOLUCIONES SÓLIDAS DE COMPOSICIÓN CERCANA AL INP O INGAAS NO CAMBIO DESPUÉS DEL RECOCIDO. PARA COMPOSICIONES CERCANAS AL CENTRO DE LA REGION EN QUE LA CONSTANTE RETICULAR DE LAS CAPAS ES IGUAL A LA DEL INP, EL CAMBIO FUE MUY NOTORIO DEBIDO A LA APARICIÓN DE UN PICO ADICIONAL EN EL ESPECTRO DE FOTOLUMINISCENCIA. ESTO PODRÍA RELACIONARSE CON LA DESCOMPOSICIÓN DE AQUELLAS SOLUCIONES SÓLIDAS CUYA COMPOSICIÓN ESTA DENTRO DE UNA BRECHA DE MISCIBILIDAD PREDICHA TEÓRICAMENTE. PARA EVITAR LA DEGRADACIÓN DE LAS CAPAS EPITAXIALES, CAUSADA POR LA EVAPORACIÓN DE FÓSFORO DURANTE EL RECOCIDO, SU SUPERFICIE SE RECUBRIÓ CON CAPAS DE SIO2 DEPOSITADO DE UNA EMULSIÓN.AbstractINGAASP; SOLID SOLUTION; MISCIBILITY GAP; DECOMPOSITION AND PHOTOLUMINESCENCE.es-ES
dc.descriptionTHE INFLUENCE OF THERMAL TREATMENTS ON THE PHOTOLUMINESCENCE SPECTRA OF IN1−XGAXASYP1−YEPITAXIAL LAYERS OF VARIOUS COMPOSITIONS GROWN BY LPE ON INP SUBSTRATES HAS BEEN STUDIED. TO PREVENT THE EPITAXIAL LAYERS FROM DEGRADATION, DUE TO PHOSPHOR EVAPORATION DURING THE BAKING, THEIR SURFACE WAS COVERED BY SPIN-ON SIO2 LAYERS. THE PHOTOLUMINESCENCE SPECTRA DID NOT CHANGE FOR SOLID SOLUTIONS WHOSE COMPOSITIONS WERE NEAR INP AND INGAAS. FOR COMPOSITIONS IN THE MIDDLE OF THE LATTICE-MATCHED REGION, THE VARIATIONS WERE VERY NOTICEABLE BECAUSE THE APPEARANCE OF ADDITIONAL PEAKS IN THE LUMINESCENCE SPECTRA. THIS COULD BE RELATED TO THE DECOMPOSITION OF THOSE SOLID SOLUTIONS WHOSE COMPOSITIONS LIE INSIDE A THEORETICALLY PREDICTED MISCIBILITY GAP.en-US
dc.formatapplication/pdf
dc.languagespa
dc.publisherRevista Mexicana de Físicaes-ES
dc.relationhttp://ojs.unam.mx/index.php/rmf/article/view/13981/13318
dc.sourceRevista Mexicana de Física; Vol 50, No 003 (2004)es-ES
dc.subjectINGAASP; SOLUCION SOLIDA; BRECHA DE MISCIBILIDAD; DESCOMPOSICION Y FOTOLUMINISCENCIAes-ES
dc.subjectINGAASP; SOLID SOLUTION; MISCIBILITY GAP; DECOMPOSITION AND PHOTOLUMINESCENCE.en-US
dc.titleInfluence of baking on the photoluminescence spectra of in11x xgaxasyp11y solid solutions grown on inp substrateses-ES
dc.typeArtículos de revistas