Fabrication and characterization of silver nanostructures conformal coating layer onto electrospun N6 nanofibers with improved physical properties
(KLUWER ACADEMIC PUBLISHERS, 2014-01-01)
In this communication, colloidal silver (Ag) nanostructures were synthesized and deposited directly onto electrospun nylon 6 (N6) fibers without using surface modifier in the form of an ultrathin conformal coating layer ...
TiO2 nanorods coated onto nylon 6 nanofibers using hydrothermal treatment with improved mechanical properties
(ELSEVIER B.V., 2014-09-05)
Well-aligned arrays TiO2 nanorods were deposited onto electrospun nylon 6 (N6) nanofibers. The complete coverage of individual fiber surfaces with TiO2 nanorods occurred in a very short time using a cost effective hydrothermal ...
Heterophase polymerization of different methacrylates: Effect of alkyl ester group on kinetics and colloidal behavior
(2014)
In this article, methyl- (MMA), ethyl- (EMA), n-butyl- (BMA), n-hexyl (HMA), and 2-ethyl hexyl (2-EHMA) methacrylates were homopolymerized in heterophase at 60�C using sodium dodecyl sulfate as surfactant and potassium ...
Heterophase polymerization of different methacrylates: Effect of alkyl ester group on kinetics and colloidal behavior
(2014)
In this article, methyl- (MMA), ethyl- (EMA), n-butyl- (BMA), n-hexyl (HMA), and 2-ethyl hexyl (2-EHMA) methacrylates were homopolymerized in heterophase at 60°C using sodium dodecyl sulfate as surfactant and potassium ...
Coagulation-flocculation of colloidal suspensions of kaolinite, bentonite, and alumina by chitosan sulfate
(2012)
This article reports on the removal of colloidal suspensions of kaolinite, bentonite, and alumina using chitosan sulfate (ChS). ChS was synthesized by partial introduction of sulfate groups in the chitosan (Ch) structure. ...
Coagulation-flocculation of colloidal suspensions of kaolinite, bentonite, and alumina by chitosan sulfate
(2012)
This article reports on the removal of colloidal suspensions of kaolinite, bentonite, and alumina using chitosan sulfate (ChS). ChS was synthesized by partial introduction of sulfate groups in the chitosan (Ch) structure. ...
A broad pH range and processive chitinase from a metagenome library
(Associação Brasileira de Divulgação Científica, 2017)
Semicontinuous microemulsion copolymerization of vinyl acetate and butyl acrylate: High solid content and effect of monomer addition rate
(2009)
Vinyl acetate and butyl acrylate were copolymerized in microemulsion under monomer-starved conditions by a semicontinuous process using different monomer addition rates (Ra). A mixture of sodium dodecyl sulfate and ...
Semicontinuous microemulsion copolymerization of vinyl acetate and butyl acrylate: High solid content and effect of monomer addition rate
(2009)
Vinyl acetate and butyl acrylate were copolymerized in microemulsion under monomer-starved conditions by a semicontinuous process using different monomer addition rates (Ra). A mixture of sodium dodecyl sulfate and ...