Effect of cobalt(II) oxide and manganese(IV) oxide on sintering of tin(IV) oxide
(1996-03-01)
Additions of 0.5 to 2.0 mol% of CoO or MnO2 onto SnO, promote densification of this oxide up to 99% of theoretical density. The temperature of the maximum shrinkage rate (TM) and the relative density in the maximum ...
Effect of cobalt(II) oxide and manganese(IV) oxide on sintering of tin(IV) oxide
(1996-03-01)
Additions of 0.5 to 2.0 mol% of CoO or MnO2 onto SnO, promote densification of this oxide up to 99% of theoretical density. The temperature of the maximum shrinkage rate (TM) and the relative density in the maximum ...
FLUORESCENCE-SPECTRA OF ANTHRACENE DISSOLVED IN VINYLIC AND OLEFINIC POLYMERS
(Soc Brasileira QuimicaSao PauloBrasil, 1995)
STUDY OF MISCIBILITY OF POLY(VINYL ACETATE) AND POLY(VINYL ALCOHOL) BLENDS BY FLUORESCENCE SPECTROSCOPY
(John Wiley & Sons IncNew York, 1995)
STUDY OF SECONDARY RELAXATIONS OF POLYETHYLENE BY PHOTOLUMINESCENCE TECHNIQUE
(Pergamon-elsevier Science LtdOxfordInglaterra, 1993)
Microscopic and dielectric analyses of vanadium and tungsten modified barium zirconium titanate ceramics
(2010-12-01)
Dielectric spectroscopy was used in this study to examine polycrystalline vanadium and tungstendoped BaZr 0.1Ti 0.90O 3 (BZT10:2V and BZT10:2W) ceramics obtained by the mixed oxide method. According to X-ray diffraction ...
Microscopic and dielectric analyses of vanadium and tungsten modified barium zirconium titanate ceramics
(2010-12-01)
Dielectric spectroscopy was used in this study to examine polycrystalline vanadium and tungstendoped BaZr 0.1Ti 0.90O 3 (BZT10:2V and BZT10:2W) ceramics obtained by the mixed oxide method. According to X-ray diffraction ...
Impedance spectroscopy of SnO2: CoO during sintering
(Elsevier B.V., 1997-01-01)
SnO2:m mol% CoO (0.5 less than or equal to m less than or equal to 6.0) ceramic specimens were studied by impedance spectroscopy in the 5 Hz-13 MHz frequency range during heating cold-pressed specimens from room temperature ...
Impedance spectroscopy of SnO2: CoO during sintering
(Elsevier B.V., 1997-01-01)
SnO2:m mol% CoO (0.5 less than or equal to m less than or equal to 6.0) ceramic specimens were studied by impedance spectroscopy in the 5 Hz-13 MHz frequency range during heating cold-pressed specimens from room temperature ...