Artículos de revistas
Comparison Of Silorane And Methacrylate-based Composites On The Polymerization Heat Generated With Different Lightcuring Units And Dentin Thicknesses
Registro en:
Brazilian Dental Journal. , v. 24, n. 3, p. 258 - 262, 2013.
1036440
10.1590/0103-6440201301904
2-s2.0-84881508770
Autor
Guiraldo R.D.
Consani S.
Consani R.L.X.
Berger S.B.
Correr A.B.
Sinhoreti M.A.C.
Correr-Sobrinho L.
Institución
Resumen
This study evaluated the temperature variation in the pulp chamber during photoactivation of two restorative composite resins (Filtek P90 silorane-based composite and Heliomolar methacrylate-based composite) with either a quartz-tungsten-halogen (QTH) or lightemitting diodes (LED) light-curing unit (LCU) and using dentin thicknesses (0.5 and 1.0 mm). Standardized cavities (2×2×2 mm) were prepared in 80 bovine incisors, which were randomly assigned to 8 groups according to the photoactivation method and dentin thickness. Filtek P90 and Heliomolar (both in shade A3) were used with their respective adhesive systems (P90 self-etch primer / P90 adhesive bond and Excite adhesive). All experiments were carried out in a controlled environment (37°C). The temperature variations (°C) were recorded using a digital thermometer attached to a K-type thermocouple. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). For composite/ dentin thickness interaction, temperature increase was significantly higher in 0.5 mm dentin thickness (40.07°C) compared with 1.0 mm dentin thickness (39.61°C) for Filtek P90. For composite/LCU interaction, the temperature increase was significantly higher for Filtek P90 (39.21°C - QTH and 40.47°C - LED) compared with Heliomolar (38.40°C - QTH and 39.30°C - LED). The silorane-based composite promoted higher temperature increase in the pulp chamber than the methacrylate-based composite. 24 3 258 262 Bowen, R.L., Dental filling material comprising vinyl-silane treated fused silica and a binder consisting of the reaction product of bisphenol and glycidyl methacrylate (1962) US Patent 3,066, p. 112 Weinmann, W., Thalacher, C., Guggenberger, R., Siloranes in dental composites (2005) Dent Mater, 21, pp. 68-78 Navarra, C.O., Cadenaro, M., Armstrong, S.R., Jessop, J., Antoniolli, F., Sergo, V., Degree of conversion of Filtek silorane adhesive system and Clearfil SE Bond within the hybrid and adhesive layer: An in situ Raman analysis (2009) Dent Mater, 25, pp. 1178-1185 Guiraldo, R.D., Consani, S., Consani, R.L., Berger, S.B., Mendes, W.B., Sinhoreti, M.A., Light energy transmission through composite influenced by material shades (2009) Bull Tokyo Dent Coll, 50, pp. 183-190 Guiraldo, R.D., Consani, S., Consani, R.L., Berger, S.B., Mendes, W.B., Sinhoreti, M.A., Comparison of silorane and methacrylate-based composite resins on the curing light transmission (2010) Braz Dent J, 21, pp. 538-542 Rueggeberg, F.A., Contemporary issues in photocuring (1999) Compend Contin Educ Dent Suppl, 20, pp. S4-SS15 Segreto, D., Brandt, W.C., Correr-Sobrinho, L., Sinhoreti, M.A., Consani, S., Influence of irradiance on the push-out bond strength of composite restorations photoactivated by LED (2008) J Contemp Dent Pract, 9, pp. 89-96 Guiraldo, R.D., Consani, S., Lympius, T., Schneider, L.F., Sinhoreti, M.A., Corrersobrinho, L., Influence of the light curing unit and thickness of residual dentin on generation of heat during composite photoactivation (2008) J Oral Sci, 50, pp. 137-142 Knezević, A., Tarle, Z., Meniga, A., Sutalo, J., Pichler, G., Ristić, M., Degree of conversion and temperature rise during polymerization of composite resin samples with blue diodes (2001) J Oral Rehabil, 28, pp. 586-591 Mousavinasab, S.M., Khoroushi, M., Moharreri, M., Temperature rise during primer,adhesive,and composite resin photopolymerization of a lowshrinkage composite resin under caries-like dentin lesions (2012) ISRN Dent, , [Epub ahead of print. DOI: 10.5402/2012/198351] Schneider, L.F., Consani, S., Correr-Sobrinho, L., Correr, A.B., Sinhoreti, M.A., Halogen and LED light curing of composite: Temperature increase and Knoop hardness (2006) Clin Oral Investig, 10, pp. 66-71 Guiraldo, R.D., Consani, S., de Souza, A.S., Consani, R.L., Sinhoreti, M.A., Correr-Sobrinho, L., Influence of light energy density on heat generation during photoactivation of dental composites with different dentin and composite thickness (2009) J Appl Oral Sci, 17, pp. 289-293 Guiraldo, R.D., Consani, S., Sinhoreti, M.A., Correr-Sobrinho, L., Schneider, L.F., Thermal variations in the pulp chamber associated with composite insertion techniques and light-curing methods (2009) J Contemp Dent Pract, 10, pp. 17-24 Zach, L., Cohen, G., Pulp response to externally applied heat (1965) Oral Surg Oral Med Oral Pathol, 19, pp. 515-530 Uhl, A., Volpel, A., Sigusch, B.W., Influence of heat from light curing units and dental composite polymerization on cells in vitro (2006) J Dent, 34, pp. 298-306 Masutani, S., Setcos, J.C., Schinell, R.J., Philips, R.W., Temperature rise during polymerization of visible light-activated composite resins (1988) Dent Mater, 4, pp. 174-178 Lopes, M.B., Saquy, P.C., Moura, S.K., Wang, L., Graciano, F.M., Correr Sobrinho, L., Effect of different surface penetrating sealants on the roughness of a nanofiller composite resin (2012) Braz Dent J, 23, pp. 692-697 Miletic, V., Ivanovic, V., Dzeletovic, B., Lezaja, M., Temperature changes in silorane-, ormocer-, and dimethacrylate-based composites and pulp chamber roof during light-curing (2009) J Esthet Restor Dent, 21, p. 122 Gao, B.T., Lin, H., Zheng, G., Xu, Y.X., Yang, J.L., Comparison between a siloranebased composite and methacrylate-based composites: Shrinkage characteristics, thermal properties, gel point and vitrification point (2012) Dent Mater J, 31, pp. 76-85 Crivello, J., Falk, B., Zonca Jr., M.R., Photoinduced cationic ring-opening frontal polymerizations of oxetanes and oxiranes (2004) J Polym Sci, 42, pp. 1630-1646 Loney, R.W., Price, R.B., Temperature transmission of high-output light curing units through dentin (2001) Oper Dent, 26, pp. 516-520 Guiraldo, R.D., Consani, S., Mastrofrancisco, S., Consani, R.L., Sinhoreti, M.A., Correr-Sobrinho, L., Influence of light curing unit and ceramic thickness on temperature rise during resin cement photo-activation (2008) Bull Tokyo Dent Coll, 49, pp. 173-178 Pazin, M.C., Moraes, R.R., Gonçalves, L.S., Borges, G.A., Sinhoreti, M.A., Correr Sobrinho, L., Effects of ceramic thickness and curing unit on light transmission through leucite-reinforced material and polymerization of dual-cured luting agent (2008) J Oral Sci, 50, pp. 131-136