Precipitation reaction in alpha-Cu-Al-Ag alloys
(Rede Latino-Americana de Materiais, 2011-01-01)
The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, ...
Reação de precipitação de Ag na liga Cu-8%Al-6%Ag
(2008-01-01)
Ag precipitation reaction in the Cu-8wt.%Al-6wt.%Ag alloys was studied using microhardness measurements with temperature and ageing time, X-ray diffraction patterns (DRX), differential scanning calorimetry (DSC) and scanning ...
Ag-rich phase formation in the Cu-6 wt% Al alloy with Ag additions
(Pergamon-Elsevier B.V. Ltd, 2008-08-01)
Ag-rich phase formation in the Cu-6 wt% Al alloy with additions of 4, 6, 8, 10, and 12 wt% Ag was studied using microhardness changes with temperature and time, differential thermal analysis (DTA), scanning electron ...
Ag-rich phase formation in the Cu-6 wt% Al alloy with Ag additions
(Pergamon-Elsevier B.V. Ltd, 2008-08-01)
Ag-rich phase formation in the Cu-6 wt% Al alloy with additions of 4, 6, 8, 10, and 12 wt% Ag was studied using microhardness changes with temperature and time, differential thermal analysis (DTA), scanning electron ...
Effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys
(Springer, 2009-07-01)
In this work the effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys with additions of 4, 6, 8 and 10 mass% Ag was studied using differential scanning calorimetry (DSC), in ...
Effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys
(Springer, 2009-07-01)
In this work the effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys with additions of 4, 6, 8 and 10 mass% Ag was studied using differential scanning calorimetry (DSC), in ...
Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys
(Kluwer Academic Publ, 2014)
Ag-rich precipitates formation in the Cu-11%Al-10%Mn-3%Ag alloy
(Elsevier B.V., 2014-12-05)
The formation of Ag-rich precipitates in the Cu-11%Al-10%Mn-3%Ag alloy initially quenched from 1123 K was analyzed. The results showed that nanoprecipitates of a Cu-rich phase are produced at about 523 K. In higher ...
Precipitation reaction in alpha-Cu-Al-Ag alloys
(Rede Latino-Americana de Materiais, 2014)